| 注射成型 | |
| 填料：专有填料。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.50 | g/cm3 | ||
| 密度 | ASTMD792 | 1.50 | g/cm3 | ||
| 收缩率-流量(24小时) | ASTMD955 | 0.10to0.40 | % | ||
| MoldingShrinkage-AcrossFlow(24hr) | ASTMD955 | 0.60to0.90 | % | ||
| 吸水率(24hr,50%RH) | ASTMD570 | 0.090 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 0.15 | % | ||
| 拉伸模量2 | ASTMD638 | 10400 | MPa | ||
| 拉伸模量 | ISO527-2/1 | 10000 | MPa | ||
| 抗张强度3(屈服) | ASTMD638 | 120 | MPa | ||
| 拉伸应力(屈服) | ISO527-2/5 | 126 | MPa | ||
| 抗张强度3(断裂) | ASTMD638 | 120 | MPa | ||
| 拉伸应力(断裂) | ISO527-2/5 | 126 | MPa | ||
| 伸长率3(屈服) | ASTMD638 | 2.0 | % | ||
| 拉伸应变(屈服) | ISO527-2/5 | 2.2 | % | ||
| 伸长率4(断裂) | ASTMD638 | 2.0 | % | ||
| 拉伸应变(断裂) | ISO527-2/5 | 2.2 | % | ||
| 弯曲模量4(50.0mm跨距) | ASTMD790 | 9570 | MPa | ||
| 弯曲模量5 | ISO178 | 9100 | MPa | ||
| 弯曲应力 | ISO178 | 173 | MPa | ||
| 弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 179 | MPa | ||
| 弯曲强度5(断裂,50.0mm跨距) | ASTMD790 | 179 | MPa | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 100 | J/m | ||
| 悬壁梁缺口冲击强度6(23°C) | ISO180/1A | 9.6 | kJ/m2 | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD4812 | 580 | J/m | ||
| 无缺口伊佐德冲击强度5(23°C) | ISO180/1U | 39 | kJ/m2 | ||
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | ASTMD3763 | 17.6 | J | ||
| 多轴向仪器化冲击能量 | ISO6603-2 | 3.48 | J | ||
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 139 | °C | ||
| HeatDeflectionTemperature7(0.45MPa,Unannealed,64.0mmSpan) | ISO75-2/Bf | 139 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 135 | °C | ||
| 热变形温度7(1.8MPa,未退火,64.0mm跨距) | ISO75-2/Af | 135 | °C | ||
| 线形热膨胀系数-流动(-30到30°C) | ASTMD696 | 2.1E-5 | cm/cm/°C | ||
| CLTE-Transverse(-30to30°C) | ASTMD696 | 5.5E-5 | cm/cm/°C | ||
| FlameRating(1.5mm,TestingbySABIC) | UL94 | V-0 | |||
| 关于沙伯基础 LNP™ THERMOCOMP™ DX07408 compound价格 | |||||
| 1.有关“PC 沙伯基础 LNP™ THERMOCOMP™ DX07408 compound”物性表及PC塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料行情敬请关注我们的资讯动态. | |||||