长期供应LLDPE DOWLEX™ 2740G (Blown Film)原材料 ！关于DOWLEX™ 2740G (Blown Film)注塑温度(成型温度),DOWLEX™ 2740G (Blown Film)缩水率,DOWLEX™ 2740G (Blown Film)流动性等相关参数请参照美国陶氏厂家提供的物性表数据。
1、LLDPE/SABIC® LLDPE 118NJ/沙伯基础
2、LLDPE/UMERIT® 613A/日本宇部
3、mLLDPE/Eltex® PF6612KE/瑞士英力士
4、MDPE/KW Plastics KWR101-150-M5 BLK/美国KW
5、LLDPE/SABIC® LLDPE 324CNJ/沙伯基础
6、LLDPE/CERTENE™ LLHF-120C/美国Channel Prime Alliance
7、MDPE/Ravago Compounds HMP-306 (Roto)/比利时Ravago
8、LLDPE/Formolene® L62009A/台湾台化
9、LLDPE/PRE-ELEC® PE 1271/芬兰普宓斯
10、LDPE/TOTAL Polyethylene LDPE 1022 FN 24/法国TOTAL石化
以下数据由:PBT http://pbtsl.com/ 提供
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重2 | ASTMD792 | 0.940 | g/cm3 | ||
| 熔流率（熔体流动速率）2(190°C/2.16kg) | ISO1133 | 1.0 | g/10min | ||
| 薄膜厚度-经测试 | 50 | um | |||
| 膜刺穿强度3(50um) | ASTMD5748 | 2.00 | J | ||
| 膜刺穿力3(50um) | ASTMD5748 | 46.0 | N | ||
| 膜耐刺穿性3(50um) | ASTMD5748 | 4.00 | J/cm3 | ||
| 拉伸模量3 | 2%正割,MD:50um | ISO527-3 | 370 | MPa | |
| 拉伸模量3 | 2%正割,TD:50um | ISO527-3 | 420 | MPa | |
| 拉伸应力3 | MD:屈服,50um | ISO527-3 | 26.0 | MPa | |
| 拉伸应力3 | TD:屈服,50um | ISO527-3 | 25.0 | MPa | |
| 拉伸应力3 | MD:断裂,50um | ISO527-3 | 44.0 | MPa | |
| 拉伸应力3 | TD:断裂,50um | ISO527-3 | 43.0 | MPa | |
| 伸长率3 | MD:断裂,50um | ISO527-3 | 690 | % | |
| 伸长率3 | TD:断裂,50um | ISO527-3 | 740 | % | |
| 落锤冲击3(50um) | ISO7765-1/A | 120 | g | ||
| 埃尔曼多夫抗撕强度3 | MD:50um | ASTMD1922 | 130 | g | |
| 埃尔曼多夫抗撕强度3 | TD:50um | ASTMD1922 | 240 | g | |
| 薄膜厚度-经测试 | 50 | um | |||
| 膜刺穿强度3(50um) | ASTMD5748 | 2.00 | J | ||
| 膜刺穿力3(50um) | ASTMD5748 | 46.0 | N | ||
| 膜耐刺穿性3(50um) | ASTMD5748 | 4.00 | J/cm3 | ||
| 拉伸模量3 | 2%正割,MD:50um | ISO527-3 | 370 | MPa | |
| 拉伸模量3 | 2%正割,TD:50um | ISO527-3 | 420 | MPa | |
| 拉伸应力3 | MD:屈服,50um | ISO527-3 | 26.0 | MPa | |
| 拉伸应力3 | TD:屈服,50um | ISO527-3 | 25.0 | MPa | |
| 拉伸应力3 | MD:断裂,50um | ISO527-3 | 44.0 | MPa | |
| 拉伸应力3 | TD:断裂,50um | ISO527-3 | 43.0 | MPa | |
| 伸长率3 | MD:断裂,50um | ISO527-3 | 690 | % | |
| 伸长率3 | TD:断裂,50um | ISO527-3 | 740 | % | |
| 落锤冲击3(50um) | ISO7765-1/A | 120 | g | ||
| 埃尔曼多夫抗撕强度3 | MD:50um | ASTMD1922 | 130 | g | |
| 埃尔曼多夫抗撕强度3 | TD:50um | ASTMD1922 | 240 | g | |
| 维卡软化温度2 | ASTMD1525 | 125 | °C | ||
| 关于美国陶氏 DOWLEX™ 2740G (Blown Film)价格 | |||||
| 1.有关“LLDPE 美国陶氏 DOWLEX™ 2740G (Blown Film)”物性表及LLDPE塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒行情敬请关注我们的资讯动态. | |||||