长期供应PS PRL PPX-FR3原材料 ！关于PRL PPX-FR3注塑温度(成型温度),PRL PPX-FR3缩水率,PRL PPX-FR3流动性等相关参数请参照美国Polymer Resources厂家提供的物性表数据。
1、PS/Iupiace® AH80/日本三菱
2、PS/ANYPOL SE-2500/韩国SH Energy
3、PS/Adell PS IV-11-N/美国ADELL
4、PS/SUPREME Specialty PS SP6503/印度Supreme 商务设备,外壳,印刷机
5、PS/NORYL™ GFN3 resin/沙伯基础
6、PS/Bapolan® PS6260/美国Bamberger 玩具,家用货品,通用,容器
7、PP/Hostacom X M3 T15 305590/美国利安德巴塞尔
8、PS/XYRON™ 240Z/日本旭化成
9、PS/DIAREX® H350/泰国PTT
10、PS/NEFTEKHIM PS 680/俄罗斯Nizhnekamskneftekhim
以下数据由:PBT塑料 http://pbtsl.com/ 提供
| 阻燃性,耐热性，中等,自熄,无氯,无溴 注射成型 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.06 | g/cm3 | ||
| MeltMass-FlowRate(MFR)(250°C/11.6kg) | ASTMD1238 | 4.0to9.0 | g/10min | ||
| 收缩率-流动(3.18mm) | ASTMD955 | 0.50to0.70 | % | ||
| MoldingShrinkage-AcrossFlow(3.18mm) | ASTMD955 | 0.50to0.70 | % | ||
| 抗张强度(屈服,3.17mm) | ASTMD638 | 64.1 | MPa | ||
| TensileStrength(Break,3.18mm) | ASTMD638 | 62.1 | MPa | ||
| 伸长率(屈服,3.18mm) | ASTMD638 | 5.0 | % | ||
| 伸长率(断裂,3.18mm) | ASTMD638 | 25 | % | ||
| 弯曲模量(3.17mm) | ASTMD790 | 2410 | MPa | ||
| 弯曲强度(3.18mm) | ASTMD790 | 89.6 | MPa | ||
| 简支梁缺口冲击强度(23°C) | ISO179/1 | 15 | kJ/m2 | ||
| 悬壁梁缺口冲击强度 | -30°C,3.18mm | ASTMD256 | 110 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 210 | J/m | |
| 悬壁梁缺口冲击强度(23°C) | ISO180/1A | 15 | kJ/m2 | ||
| 落锤冲击(3.18mm) | ASTMD3029 | 16.9 | J | ||
| 载荷下热变形温度(0.45MPa,未退火,3.18mm) | ASTMD648 | 129 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火,3.18mm) | ASTMD648 | 121 | °C | ||
| 维卡软化温度 | ASTMD15252 | 135 | °C | ||
| RTIElec | 0.75mm | UL746 | 65.0 | °C | |
| RTIElec | 1.5mm | UL746 | 110 | °C | |
| RTIElec | 1.7mm | UL746 | 110 | °C | |
| RTIElec | 3.0mm | UL746 | 110 | °C | |
| RTIImp | 0.75mm | UL746 | 65.0 | °C | |
| RTIImp | 1.5mm | UL746 | 105 | °C | |
| RTIImp | 1.7mm | UL746 | 105 | °C | |
| RTIImp | 3.0mm | UL746 | 105 | °C | |
| RTIStr | 0.75mm | UL746 | 65.0 | °C | |
| RTIStr | 1.5mm | UL746 | 110 | °C | |
| RTIStr | 1.7mm | UL746 | 110 | °C | |
| RTIStr | 3.0mm | UL746 | 110 | °C | |
| 体积电阻率 | ASTMD257 | 1.0E+17 | ohmscm | ||
| 介电强度(3.00mm) | ASTMD149 | 24 | kV/mm | ||
| ComparativeTrackingIndex(CTI)(0.750mm) | UL746 | PLC2 | |||
| 高电弧燃烧指数(HAI) | 1.5mm | UL746 | PLC1 | ||
| 高电弧燃烧指数(HAI) | 1.7mm | UL746 | PLC1 | ||
| 高电弧燃烧指数(HAI) | 3.0mm | UL746 | PLC1 | ||
| HighVoltageArcTrackingRate(HVTR)(0.750mm) | UL746 | PLC3 | |||
| 热丝引燃(HWI) | 1.5mm | UL746 | PLC0 | ||
| 热丝引燃(HWI) | 1.7mm | UL746 | PLC0 | ||
| 热丝引燃(HWI) | 3.0mm | UL746 | PLC0 | ||
| UL阻燃等级 | 0.75mm,BK | UL94 | V-2 | ||
| UL阻燃等级 | 1.5mm,ALL | UL94 | V-1 | ||
| UL阻燃等级 | 1.7mm,ALL | UL94 | V-1 | ||
| UL阻燃等级 | 3.0mm,ALL | UL94 | V-1 | ||
| 关于美国Polymer Resources PRL PPX-FR3价格 | |||||
| 1.有关“PS 美国Polymer Resources PRL PPX-FR3”物性表及PS塑料原料价格以出厂实时数据为准. 2.更多塑料原料行情敬请关注我们的资讯动态. | |||||