长期供应共聚多酯 Tritan™ FX200原材料 ！关于Tritan™ FX200注塑温度(成型温度),Tritan™ FX200缩水率,Tritan™ FX200流动性等相关参数请参照美国Eastman厂家提供的物性表数据。
1、TPU/Mirakutoran® TPU P485/日本美拉龙
2、EMAA/Conpol™ 20B/美国杜邦
3、TPU/Quadraflex™ ALE-75A-B30/美国Biomerics
以下数据由:PBT塑料 http://pbtsl.com/ 提供
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.19 | g/cm3 | ||
| WaterAbsorption(23°C,24hr,0.254mm) | ASTMD570 | 0.50 | % | ||
| TaberAbrasionResistance2(23°C,250.0um) | ASTMD1044 | 20Haze | % | ||
| 薄膜厚度-经测试 | 250 | um | |||
| 膜刺穿强度3(250um) | ASTMD3763 | 4.50 | J | ||
| 割线模量-MD(250um) | ASTMD882 | 1500 | MPa | ||
| SecantModulus-TD(250um) | ASTMD882 | 1400 | MPa | ||
| 抗张强度-MD(屈服,250um) | ASTMD882 | 43.0 | MPa | ||
| TensileStrength-TD(Yield,250um) | ASTMD882 | 41.0 | MPa | ||
| TensileStrength-MD(Break,250um) | ASTMD882 | 57.0 | MPa | ||
| TensileStrength-TD(Break,250um) | ASTMD882 | 42.0 | MPa | ||
| TensileElongation-MD(Yield,250um) | ASTMD882 | 8.0 | % | ||
| TensileElongation-TD(Yield,250um) | ASTMD882 | 8.0 | % | ||
| 伸长率-MD(断裂,250um) | ASTMD882 | 110 | % | ||
| TensileElongation-TD(Break,250um) | ASTMD882 | 120 | % | ||
| 落锤冲击4 | -30°C,250um | ASTMD1709A | 830 | g | |
| 落锤冲击4 | -18°C,250um | ASTMD1709A | 830 | g | |
| 落锤冲击4 | 23°C,250um | ASTMD1709A | 830 | g | |
| 裤型撕裂耐性5 | MD:250um | ISO6383-1 | 10.0 | N/mm | |
| 裤型撕裂耐性5 | TD:250um | ISO6383-1 | 9.00 | N/mm | |
| 透氧率(23°C,250um,50%RH) | ASTMD3985 | 44 | cm3mm/m2/atm/24hr | ||
| 水气透过率 | 23°C,100%RH,250um | ASTMF1249 | 4.0 | g/m2/24hr | |
| 水气透过率 | 38°C,100%RH,250um | ASTMF1249 | 10 | g/m2/24hr | |
| CarbonDioxidePermeability(23°C,254.0um) | ASTMD1434 | 210 | cm3mm/m2/atm/24hr | ||
| 埃尔曼多夫抗撕强度 | MD:23°C,250.0um | ASTMD1922 | 4 | N | |
| 埃尔曼多夫抗撕强度 | TD:23°C,250.0um | ASTMD1922 | 4 | N | |
| PPTTearResistance | MD:23°C,250.0um | ASTMD2582 | 40 | N | |
| PPTTearResistance | TD:23°C,250.0um | ASTMD2582 | 40 | N | |
| 抗撕裂蔓延性 | MD:23°C,250.0um | ASTMD1938 | 310 | gf | |
| 抗撕裂蔓延性 | TD:23°C,250.0um | ASTMD1938 | 200 | gf | |
| 弹性体 | TestMethod | NominalValue | Unit | ||
| 撕裂强度 | 开裂6 | ASTMD1938 | 9.0 | kN/m | |
| 撕裂强度 | 开裂7 | ASTMD1938 | 10 | kN/m | |
| 熔融温度 | 119 | °C | |||
| 线形热膨胀系数-流动(23°C) | ASTMD696 | 8.0E-5 | cm/cm/°C | ||
| 比热 | 60°C | DSC | 1700 | J/kg/°C | |
| 比热 | 100°C | DSC | 1900 | J/kg/°C | |
| 比热 | 150°C | DSC | 2300 | J/kg/°C | |
| 比热 | 200°C | DSC | 2400 | J/kg/°C | |
| 比热 | 250°C | DSC | 2600 | J/kg/°C | |
| 光泽度(60°,250um) | ASTMD2457 | 158 | |||
| 折射率 | ASTMD542 | 1.540 | |||
| 透射率(250um) | ASTMD1003 | 93.0 | % | ||
| 雾度(250um) | ASTMD1003 | 0.80 | % | ||
| 黄度指数(250mm) | ASTMD1925 | 0.50 | YI | ||
| UVTransmittance8(250.0um) | 89 | % | |||
| 补充信息 | TestMethod | NominalValue | Unit | ||
| SurfaceEnergy | Dispersive:23°C,250.0um | ASTMD5946 | 39 | dyne/cm | |
| SurfaceEnergy | Polar:23°C,250.0um | ASTMD5946 | 8 | dyne/cm | |
| SurfaceEnergy | Total:23°C,250.0um | ASTMD5946 | 47 | dyne/cm | |
| 关于美国Eastman Tritan™ FX200价格 | |||||
| 1.有关“共聚多酯 美国Eastman Tritan™ FX200”物性表及共聚多酯塑料原料价格以出厂实时数据为准. 2.更多塑料原料行情敬请关注我们的资讯动态. | |||||