长期供应共聚多酯 Spectar™ Clear Copolyester原材料 ！关于Spectar™ Clear Copolyester注塑温度(成型温度),Spectar™ Clear Copolyester缩水率,Spectar™ Clear Copolyester流动性等相关参数请参照美国Eastman厂家提供的物性表数据。
1、EMAA/Surlyn® 8940/美国杜邦
2、TPU/Mirakutoran® TPU E595PUOO/日本美拉龙
3、TPU/Jamplast JPTPUPE/美国Jamplast
以下数据由:PBT http://pbtsl.com/ 提供
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 密度 | ASTMD1505 | 1.23 | g/cm3 | ||
| 吸水率(23°C,24hr,3.00mm) | ASTMD570 | 0.19 | % | ||
| 固有粘度2(23°C) | 内部方法 | 0.73 | |||
| 颜色 | a | ASTME313 | -0.15 | ||
| 颜色 | b | ASTME313 | 0.34 | ||
| 颜色 | L | ASTME313 | 96 | ||
| 洛氏硬度(R级,23°C) | ASTMD785 | 107 | |||
| 拉伸模量(23°C) | ASTMD638 | 1800 | MPa | ||
| 抗张强度 | 屈服,23°C | ASTMD638 | 48.0 | MPa | |
| 抗张强度 | 断裂,23°C | ASTMD638 | 53.0 | MPa | |
| 伸长率 | 屈服,23°C | ASTMD638 | 5.0 | % | |
| 伸长率 | 断裂,23°C | ASTMD638 | 340 | % | |
| 弯曲模量(23°C) | ASTMD790 | 2000 | MPa | ||
| 弯曲强度(23°C) | ASTMD790 | 71.0 | MPa | ||
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 83 | J/m | |
| 悬壁梁缺口冲击强度 | 0°C | ASTMD256 | 110 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 无断裂 | ||
| 无缺口悬臂梁冲击 | -30°C | ASTMD4812 | 无断裂 | ||
| 无缺口悬臂梁冲击 | 23°C | ASTMD4812 | 无断裂 | ||
| 装有测量仪表的落镖冲击 | -30°C,EnergyatPeakLoad | ASTMD3763 | 52.0 | J | |
| 装有测量仪表的落镖冲击 | 0°C,EnergyatPeakLoad | ASTMD3763 | 42.0 | J | |
| 装有测量仪表的落镖冲击 | 23°C,EnergyatPeakLoad | ASTMD3763 | 41.0 | J | |
| 载荷下热变形温度 | 0.45MPa,未退火 | ASTMD648 | 77.0 | °C | |
| 载荷下热变形温度 | 1.8MPa,未退火 | ASTMD648 | 73.0 | °C | |
| 维卡软化温度 | ASTMD1525 | 86.0 | °C | ||
| 线形热膨胀系数-流动(23°C) | ASTMD696 | 7.7E-5 | cm/cm/°C | ||
| 表面电阻率 | ASTMD257 | 1.0E+17 | ohms | ||
| 体积电阻率(23°C) | ASTMD257 | 1.0E+16 | ohmscm | ||
| 耐电弧性 | ASTMD495 | 130 | sec | ||
| StaticDecay(23°C) | ASTMD4470 | FailedtoDischarge | |||
| UL阻燃等级 | UL94 | V-2 | |||
| 光泽度(60°,3000um) | ASTMD2457 | 150 | |||
| 透射率(总计,3000um) | ASTMD1003 | 91.0 | % | ||
| 雾度(3000um) | ASTMD1003 | 0.50 | % | ||
| 黄度指数(3.00mm) | ASTMD1925 | 0.81 | YI | ||
| SheetThickness | 3.00 | mm | |||
| 关于美国Eastman Spectar™ Clear Copolyester价格 | |||||
| 1.有关“共聚多酯 美国Eastman Spectar™ Clear Copolyester”物性表及共聚多酯塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒行情敬请关注我们的资讯动态. | |||||