| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | —— | ASTMD792,ASTMD1505 | 1.27 | g/cm3 | |
| 比重 | 23°C | ISO1183/D | 1.27 | g/cm3 | |
| 吸水率(23°C,24hr) | ASTMD570,ISO62 | 0.13 | % | ||
| 洛氏硬度 | R级,23°C | ASTMD785 | 106 | ||
| 洛氏硬度 | R计秤,23°C | ISO2039-2 | 109 | ||
| 拉伸模量(23°C) | ASTMD638,ISO527-2 | 2100 | MPa | ||
| 抗张强度 | 屈服,23°C | ASTMD638,ISO527-2 | 50.0 | MPa | |
| 抗张强度 | 断裂,23°C | ASTMD638,ISO527-2 | 28.0 | MPa | |
| 伸长率 | 断裂,23°C | ASTMD638 | 130 | % | |
| 伸长率 | 断裂,23°C | ISO527-2 | 100 | % | |
| 弯曲模量 | 23°C | ASTMD790 | 2100 | MPa | |
| 弯曲模量 | 23°C | ISO178 | 2000 | MPa | |
| 弯曲应力 | 23°C | ISO178 | 68.0 | MPa | |
| 弯曲应力 | 屈服,23°C | ASTMD790 | 70.0 | MPa | |
| 薄膜厚度-经测试 | 250 | um | |||
| 割线模量 | MD:250um | ASTMD882 | 1900 | MPa | |
| 割线模量 | TD:250um | ASTMD882 | 1900 | MPa | |
| 抗张强度 | MD:屈服,250um | ASTMD882 | 52.0 | MPa | |
| 抗张强度 | TD:屈服,250um | ASTMD882 | 52.0 | MPa | |
| 抗张强度 | MD:断裂,250um | ASTMD882 | 59.0 | MPa | |
| 抗张强度 | TD:断裂,250um | ASTMD882 | 55.0 | MPa | |
| 伸长率 | MD:屈服,250um | ASTMD882 | 4.0 | % | |
| 伸长率 | TD:屈服,250um | ASTMD882 | 4.0 | % | |
| 伸长率 | MD:断裂,250um | ASTMD882 | 400 | % | |
| 伸长率 | TD:断裂,250um | ASTMD882 | 400 | % | |
| 落锤冲击2 | -18°C,250um | ASTMD1709A | 500 | g | |
| 落锤冲击2 | 23°C,250um | ASTMD1709A | 400 | g | |
| 埃尔曼多夫抗撕强度 | MD:250um | ASTMD1922 | 14 | N | |
| 埃尔曼多夫抗撕强度 | TD:250um | ASTMD1922 | 17 | N | |
| 裤型撕裂耐性3 | MD:250um | ISO6383-1 | 36.0 | N/mm | |
| 裤型撕裂耐性3 | TD:250um | ISO6383-1 | 36.0 | N/mm | |
| 透氧率(23°C,250um,50%RH) | ASTMD3985 | 10 | cm3mm/m2/atm/24hr | ||
| 水气透过率(38°C,100%RH,250um) | ASTMF1249 | 7.0 | g/m2/24hr | ||
| CarbonDioxidePermeability(23°C,250.0um) | ASTMD1434 | 49 | cm3mm/m2/atm/24hr | ||
| PPTTearResistance | MD:23°C,250mm | ASTMD2582 | 93 | N | |
| PPTTearResistance | TD:23°C,250mm | ASTMD2582 | 93 | N | |
| 抗撕裂蔓延性 | SplitTearMethod,MD:23°C,250mm | ASTMD1938 | 36 | kN/m | |
| 抗撕裂蔓延性 | SplitTearMethod,TD:23°C,250mm | ASTMD1938 | 36 | kN/m | |
| 薄膜厚度-经测试 | 250 | um | |||
| 割线模量 | MD:250um | ASTMD882 | 1900 | MPa | |
| 割线模量 | TD:250um | ASTMD882 | 1900 | MPa | |
| 抗张强度 | MD:屈服,250um | ASTMD882 | 52.0 | MPa | |
| 抗张强度 | TD:屈服,250um | ASTMD882 | 52.0 | MPa | |
| 抗张强度 | MD:断裂,250um | ASTMD882 | 59.0 | MPa | |
| 抗张强度 | TD:断裂,250um | ASTMD882 | 55.0 | MPa | |
| 伸长率 | MD:屈服,250um | ASTMD882 | 4.0 | % | |
| 伸长率 | TD:屈服,250um | ASTMD882 | 4.0 | % | |
| 伸长率 | MD:断裂,250um | ASTMD882 | 400 | % | |
| 伸长率 | TD:断裂,250um | ASTMD882 | 400 | % | |
| 落锤冲击2 | -18°C,250um | ASTMD1709A | 500 | g | |
| 落锤冲击2 | 23°C,250um | ASTMD1709A | 400 | g | |
| 埃尔曼多夫抗撕强度 | MD:250um | ASTMD1922 | 14 | N | |
| 埃尔曼多夫抗撕强度 | TD:250um | ASTMD1922 | 17 | N | |
| 裤型撕裂耐性3 | MD:250um | ISO6383-1 | 36.0 | N/mm | |
| 裤型撕裂耐性3 | TD:250um | ISO6383-1 | 36.0 | N/mm | |
| 透氧率(23°C,250um,50%RH) | ASTMD3985 | 10 | cm3mm/m2/atm/24hr | ||
| 水气透过率(38°C,100%RH,250um) | ASTMF1249 | 7.0 | g/m2/24hr | ||
| CarbonDioxidePermeability(23°C,250.0um) | ASTMD1434 | 49 | cm3mm/m2/atm/24hr | ||
| PPTTearResistance | MD:23°C,250mm | ASTMD2582 | 93 | N | |
| PPTTearResistance | TD:23°C,250mm | ASTMD2582 | 93 | N | |
| 关于美国Eastman Eastman™ 1223价格 | |||||
| 1.有关“共聚多酯 美国Eastman Eastman™ 1223”物性表及共聚多酯塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料行情敬请关注我们的资讯动态. | |||||