长期供应共聚多酯 Tritan™ LX200原材料 ！关于Tritan™ LX200注塑温度(成型温度),Tritan™ LX200缩水率,Tritan™ LX200流动性等相关参数请参照美国Eastman厂家提供的物性表数据。
1、EMAA/Nucrel® 925/美国杜邦
2、TPU/Elastollan® 1195 A/德国巴斯夫
3、EVOH/EVAL™ E171B/比利时EVAL
4、TPU/Mirakutoran® TPU P26M/日本美拉龙
以下数据由:PBT塑胶原料 http://pbtsl.com/ 提供
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 透射率 | % | 86.9到92.1 | |||
| 雾度 | % | 0.20到2.3 | |||
| 光泽度 | 107到162 | ||||
| 23℃ | J/m | 0.008到0.351 | |||
| 23℃ | J | 7.33到24.19 | |||
| 23℃ | kJ/m2 | 0.975到27.393 | |||
| 23℃ | N.m | 2132.74到4858.41 | |||
| —— | 1.13到1.34 | ||||
| 吸水率(23℃,24hr) | % | 0.12到0.50 | |||
| 收缩率-流动(23℃) | mm/mm | 50.8E-3到154.9E-3 | |||
| 23℃ | g/cm3 | 1.23到1.27 | |||
| —— | g/cm3 | 1.19到1.33 | |||
| 1.8Mpa,未退火 | °C | 62到65 | |||
| 0.45Mpa,未退火 | °C | 70到73 | |||
| 导热系数(23℃) | W/m2k | 0.23到0.26 | |||
| 线形热膨胀系数-流动 | mm/mm/°C | 71.1E-5到203.2E-5 | |||
| —— | °C | 66到89 | |||
| —— | °C | 78到89 | |||
| 1.8Mpa,未退火 | °C | 62到92 | |||
| 玻璃转化温度 | °C | 71到110 | |||
| 0.45Mpa,未退火 | °C | 65到110 | |||
| 断裂,23℃ | % | 97到230 | |||
| 23℃ | Mpa | 59.03到68.0 | |||
| 23℃ | Mpa | 1510.34到1951.72 | |||
| 屈服,23℃ | % | 4.0到7.0 | |||
| 屈服,23℃ | % | 4.0到7.4 | |||
| 23℃ | Mpa | 1496.55到2537.93 | |||
| 屈服,23℃ | Mpa | 62.0到77.93 | |||
| 23℃ | Mpa | 64.76到77.93 | |||
| 断裂,23℃ | Mpa | 27.45到58.0 | |||
| 断裂,23℃ | Mpa | 23.38到53.17 | |||
| 屈服,23℃ | Mpa | 43.03到50.0 | |||
| 23℃ | Mpa | 1496.55到2117.24 | |||
| 断裂,23℃ | % | 30到340 | |||
| 屈服,23℃ | Mpa | 42.28到58.0 | |||
| 23℃ | Mpa | 1496.55到2117.24 | |||
| 洛氏硬度(23℃) | 103到115 | ||||
| 肖氏硬度(23℃) | 55到95 | ||||
| MD:断裂 | Mpa | 23.03到59.59 | |||
| MD | Mpa | 1496.55到2200.0 | |||
| MD | g | 25到1400 | |||
| 水气透过率 | g/100 | 0.15到8.7 | |||
| 落锤冲击(23℃) | g | 390到880 | |||
| 断裂,23℃ | Mpa | 20.0到45.03 | |||
| TD:断裂 | Mpa | 18.14到58.9 | |||
| TD:屈服 | Mpa | 38.69到52.41 | |||
| 裤型撕裂耐性 | n/m | 523.01到1823.01 | |||
| 透氧率(23℃) | cm3mil/100 | 25到84 | |||
| MD:屈服 | % | 3.0到7.3 | |||
| TD:断裂 | % | 4.0到550 | |||
| 断裂,23℃ | % | 38到710 | |||
| 薄膜厚度-经测试 | mil | 0.98到13 | |||
| TD | Mpa | 1241.38到2124.14 | |||
| TD | g | 12到1700 | |||
| TD:屈服 | % | 4.0到7.3 | |||
| MD:屈服 | Mpa | 40.76到52.0 | |||
| MD:断裂 | % | 4.0到410 | |||
| 耐电弧性 | sec | 128到158 | |||
| 介电强度(23℃) | V/mil | 400到410 | |||
| 介电常数(23℃) | 2.40到3.20 | ||||
| 耗散因数(23℃) | 4.7E-3到0.020 | ||||
| 关于美国Eastman Tritan™ LX200价格 | |||||
| 1.有关“共聚多酯 美国Eastman Tritan™ LX200”物性表及共聚多酯塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒行情敬请关注我们的资讯动态. | |||||