长期供应共聚多酯 Tritan™ FX100原材料 ！关于Tritan™ FX100注塑温度(成型温度),Tritan™ FX100缩水率,Tritan™ FX100流动性等相关参数请参照美国Eastman厂家提供的物性表数据。
1、TPU/Mirakutoran® TPU P190/日本美拉龙
2、EMAA/Surlyn® 8660/美国杜邦
3、TPU/Ravathane R210A80UV/比利时Ravago
4、TPU/Elastollan® 1185 A HFFR/德国巴斯夫 薄膜,电缆护套
以下数据由:PBT塑料 http://pbtsl.com/ 提供
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.19 | g/cm3 | ||
| 吸水率(23°C,24hr,0.250mm) | ASTMD570 | 0.50 | % | ||
| 耐磨耗性2(23°C) | ASTMD1044 | 23haze | % | ||
| 薄膜厚度-经测试 | 250 | um | |||
| 膜刺穿强度3(250um) | ASTMD3763 | 4.60 | J | ||
| 割线模量 | MD:250um | ASTMD882 | 1500 | MPa | |
| 割线模量 | TD:250um | ASTMD882 | 1400 | MPa | |
| 抗张强度 | MD:屈服,250um | ASTMD882 | 41.0 | MPa | |
| 抗张强度 | TD:屈服,250um | ASTMD882 | 40.0 | MPa | |
| 抗张强度 | MD:断裂,250um | ASTMD882 | 59.0 | MPa | |
| 抗张强度 | TD:断裂,250um | ASTMD882 | 52.0 | MPa | |
| 伸长率 | MD:屈服,250um | ASTMD882 | 7.0 | % | |
| 伸长率 | TD:屈服,250um | ASTMD882 | 7.0 | % | |
| 伸长率 | MD:断裂,250um | ASTMD882 | 180 | % | |
| 伸长率 | TD:断裂 | ASTMD882 | 200 | % | |
| 落锤冲击4 | -30°C,250um | ASTMD1709A | 910 | g | |
| 落锤冲击4 | 23°C,250um | ASTMD1709A | 880 | g | |
| 裤型撕裂耐性5 | MD:250um | ISO6383-1 | 11.0 | N/mm | |
| 裤型撕裂耐性5 | TD:250um | ISO6383-1 | 11.0 | N/mm | |
| 透氧率(23°C,250um,50%RH) | ASTMD3985 | 32 | cm3mm/m2/atm/24hr | ||
| 水气透过率 | 23°C,100%RH,250um | ASTMF1249 | 4.0 | g/m2/24hr | |
| 水气透过率 | 38°C,100%RH,250um | ASTMF1249 | 11 | g/m2/24hr | |
| CarbonDioxidePermeability6(23°C,254.0um) | ASTMD1434 | 150 | cm3mm/m2/atm/24hr | ||
| ElmendorfTearStrength | MD:23°C,250.0um | ASTMD1922 | 5 | N | |
| ElmendorfTearStrength | TD:23°C,250.0um | 6 | N | ||
| PPTTearResistance | MD:23°C,250.0um | ASTMD2582 | 42 | N | |
| PPTTearResistance | TD:23°C,250.0um | ASTMD2582 | 56 | N | |
| 抗撕裂蔓延性7 | MD:23°C,250.0um | ASTMD1938 | 410 | gf | |
| 抗撕裂蔓延性7 | TD:23°C,250.0um | ASTMD1938 | 310 | gf | |
| 薄膜厚度-经测试 | 250 | um | |||
| 膜刺穿强度3(250um) | ASTMD3763 | 4.60 | J | ||
| 割线模量 | MD:250um | ASTMD882 | 1500 | MPa | |
| 割线模量 | TD:250um | ASTMD882 | 1400 | MPa | |
| 抗张强度 | MD:屈服,250um | ASTMD882 | 41.0 | MPa | |
| 抗张强度 | TD:屈服,250um | ASTMD882 | 40.0 | MPa | |
| 抗张强度 | MD:断裂,250um | ASTMD882 | 59.0 | MPa | |
| 抗张强度 | TD:断裂,250um | ASTMD882 | 52.0 | MPa | |
| 伸长率 | MD:屈服,250um | ASTMD882 | 7.0 | % | |
| 伸长率 | TD:屈服,250um | ASTMD882 | 7.0 | % | |
| 伸长率 | MD:断裂,250um | ASTMD882 | 180 | % | |
| 伸长率 | TD:断裂 | ASTMD882 | 200 | % | |
| 落锤冲击4 | -30°C,250um | ASTMD1709A | 910 | g | |
| 落锤冲击4 | 23°C,250um | ASTMD1709A | 880 | g | |
| 裤型撕裂耐性5 | MD:250um | ISO6383-1 | 11.0 | N/mm | |
| 裤型撕裂耐性5 | TD:250um | ISO6383-1 | 11.0 | N/mm | |
| 透氧率(23°C,250um,50%RH) | ASTMD3985 | 32 | cm3mm/m2/atm/24hr | ||
| 水气透过率 | 23°C,100%RH,250um | ASTMF1249 | 4.0 | g/m2/24hr | |
| 水气透过率 | 38°C,100%RH,250um | ASTMF1249 | 11 | g/m2/24hr | |
| CarbonDioxidePermeability6(23°C,254.0um) | ASTMD1434 | 150 | cm3mm/m2/atm/24hr | ||
| ElmendorfTearStrength | MD:23°C,250.0um | ASTMD1922 | 5 | N | |
| ElmendorfTearStrength | TD:23°C,250.0um | 6 | N | ||
| PPTTearResistance | MD:23°C,250.0um | ASTMD2582 | 42 | N | |
| PPTTearResistance | TD:23°C,250.0um | ASTMD2582 | 56 | N | |
| 抗撕裂蔓延性7 | MD:23°C,250.0um | ASTMD1938 | 410 | gf | |
| 抗撕裂蔓延性7 | TD:23°C,250.0um | ASTMD1938 | 310 | gf | |
| 撕裂强度 | 开裂8 | ASTMD1938 | 12 | kN/m | |
| 撕裂强度 | 开裂9 | ASTMD1938 | 13 | kN/m | |
| 熔融温度 | 110 | °C | |||
| 线形热膨胀系数-流动(23°C,0.250mm) | ASTMD696 | 9.0E-5 | cm/cm/°C | ||
| 比热 | 60°C | DSC | 1700 | J/kg/°C | |
| 关于美国Eastman Tritan™ FX100价格 | |||||
| 1.有关“共聚多酯 美国Eastman Tritan™ FX100”物性表及共聚多酯塑料原料价格以出厂实时数据为准. 2.更多塑料原料行情敬请关注我们的资讯动态. | |||||