长期供应CAB Tenite™ Butyrate 485E3720023 Clear, Trsp原材料 ！关于Tenite™ Butyrate 485E3720023 Clear, Trsp注塑温度(成型温度),Tenite™ Butyrate 485E3720023 Clear, Trsp缩水率,Tenite™ Butyrate 485E3720023 Clear, Trsp流动性等相关参数请参照美国Eastman厂家提供的物性表数据。
1、氟橡胶/DAI-EL™ G-701/大金氟化工
2、PC/ABS/LNP™ STAT-KON™ DX07323 compound/沙伯基础 填料：专有填料。
3、PP/FORMULA P FIB 3620/L/德国Putsch Kunststoffe
4、PVDF/3M™ Dyneon™ Fluoroplastic PVDF 60120000/美国3M
5、PMMA/LNP™ STAT-LOY™ 9X05426C compound/沙伯基础
6、PVDF/Kynar® LBG/法国阿科玛
7、PP/MAJORIS FW195X - 1298/法国AD MAJORIS
8、pur未指定/PMC® 780 Dry/Wet/美国Smooth-On
9、氟橡胶/3M™ Dyneon™ Fluoroelastomer FE 5620N/美国3M
10、氟橡胶/Viton® Extreme™ ETP-600S/美国科慕化学
以下数据由:PBT http://pbtsl.com/ 提供
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.16 | g/cm3 | ||
| 收缩率-流动 | ASTMD955 | 0.20to0.60 | % | ||
| 吸水率(23°C,24hr) | ASTMD570 | 1.2 | % | ||
| 抗张强度(屈服,23°C) | ASTMD638 | 17.2 | MPa | ||
| 抗张强度(断裂,23°C) | ASTMD638 | 20.0 | MPa | ||
| 伸长率(断裂,23°C) | ASTMD638 | 50 | % | ||
| 弯曲模量(23°C) | ASTMD790 | 827 | MPa | ||
| 弯曲强度(屈服,23°C) | ASTMD790 | 21.4 | MPa | ||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 120 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 450 | J/m | |
| DeflectionTemperatureUnderLoad2(0.45MPa,Annealed) | ASTMD648 | 68.0 | °C | ||
| DeflectionTemperatureUnderLoad2(1.8MPa,Annealed) | ASTMD648 | 52.0 | °C | ||
| 维卡软化温度2 | ASTMD1525 | 88.0 | °C | ||
| 线形热膨胀系数-流动(23°C) | ASTMD696 | 2.0E-5 | cm/cm/°C | ||
| 比热(23°C) | DSC | 1260to1670 | J/kg/°C | ||
| 导热系数3(23°C) | ASTMC177 | 0.25 | W/m/K | ||
| 介电强度(23°C) | ASTMD149 | 12to19 | kV/mm | ||
| 介电常数(23°C,1MHz) | ASTMD150 | 3.30to3.80 | |||
| 耗散因数(23°C,1MHz) | ASTMD150 | 0.010to0.15 | |||
| 折射率 | ASTMD542 | 1.460to1.490 | |||
| 透射率(1520um) | ASTMD1003 | >90.0 | % | ||
| 雾度(1520um) | ASTMD1003 | <8.5 | % | ||
| 补充信息 | TestMethod | NominalValue | Unit | ||
| SolubleMatterLoss(23°C) | ASTMD570 | 0.10 | % | ||
| WeightLossonHeating-72hrs(80°C) | ASTMD707 | 1.2 | % | ||