长期供应HDPE SCLAIR® 19C原材料 !关于SCLAIR® 19C注塑温度(成型温度),SCLAIR® 19C缩水率,SCLAIR® 19C流动性等相关参数请参照加拿大NOVA Chemicals厂家提供的物性表数据。
1、HDPE/Premier HD30H18/美国Premier Polymers
2、AS(SAN)/CERTENE™ 705 SAN/美国Channel Prime Alliance
3、HDPE/Purell GB7250/美国利安德巴塞尔
4、HDPE/NOVAPOL® HB-W555-AC/加拿大NOVA Chemicals 包装,食品包装
5、HDPE/NEXUS PE HDPE-2052/美国Nexus
6、ASA/UNIBRITE® UA-1200/日本住友诺格
7、HDPE/PRE-ELEC® PE 1250/芬兰普宓斯
8、HDPE/Premier HD11051/美国Premier Polymers
9、HDPE/Eleme HBG00346/尼日利亚Eleme
10、AS(SAN)/Kostil® B 266/意大利Versalis
以下数据由:PBT塑料颗粒 http://pbtsl.com/ 提供
高密度,清晰度,高,食品接触的合规性,均聚物,刚性,高,低速凝固晶点,阻隔树脂 共挤出成型,薄膜挤出 | |
薄膜,混合,食品包装 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
比重 | ASTMD792 | 0.958 | g/cm3 | ||
熔流率(熔体流动速率)(190°C/2.16kg) | ASTMD1238 | 0.95 | g/10min | ||
薄膜厚度-经测试 | 38 | um | |||
SecantModulus-1%Secant,MD(38um,BlownFilm) | ASTMD882 | 840 | MPa | ||
SecantModulus-1%Secant,TD(38um,BlownFilm) | ASTMD882 | 1180 | MPa | ||
TensileStrength-MD(Yield,38um,BlownFilm) | ASTMD882 | 25.0 | MPa | ||
TensileStrength-TD(Yield,38um,BlownFilm) | ASTMD882 | 27.0 | MPa | ||
TensileStrength-MD(Break,38um,BlownFilm) | ASTMD882 | 42.0 | MPa | ||
TensileStrength-TD(Break,38um,BlownFilm) | ASTMD882 | 40.0 | MPa | ||
TensileElongation-MD(Break,38um,BlownFilm) | ASTMD882 | 560 | % | ||
TensileElongation-TD(Break,38um,BlownFilm) | ASTMD882 | 890 | % | ||
落锤冲击(38um,吹塑薄膜) | ASTMD1709A | 44 | g | ||
ElmendorfTearStrength-MD(38um,BlownFilm) | ASTMD1922 | 26 | g | ||
埃尔曼多夫抗撕强度-TD(38um,吹塑薄膜) | ASTMD1922 | 710 | g | ||
OxygenTransmissionRate(23°C,0%RH,38um,BlownFilm) | ASTMD3985 | 1500 | cm3/m2/24hr | ||
WaterVaporTransmissionRate(38°C,100%RH,38um,BlownFilm) | ASTMF1249 | 2.6 | g/m2/24hr | ||
肖氏硬度(邵氏D) | ASTMD2240 | 68 | |||
维卡软化温度 | ASTMD1525 | 131 | °C | ||
Gloss(45°,38.0um,BlownFilm) | ASTMD2457 | 23 | |||
雾度(38.0um,吹塑薄膜) | ASTMD1003 | 36 | % | ||
补充信息 | TestMethod | NominalValue | Unit | ||
LowFrictionPuncture-BlownFilm(38.0um) | InternalMethod | 200 | J/cm | ||
关于加拿大NOVA Chemicals SCLAIR® 19C价格 | |||||
1.有关“HDPE 加拿大NOVA Chemicals SCLAIR® 19C”物性表及HDPE塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料行情敬请关注我们的资讯动态. |